The strength and oxidation resistance of MA-X, which is a nickel base alloy, remain in temperatures up to 1200 . It also has excellent formability and weldability. Since MA-X has excellent resistance to oxidizing, reducing and neutral atmospheres, its use as heating furnace parts is particularly recommended. MA-X also is the most suitable material for jet engine tail pipes, afterburners , nozzle vein, cabin heaters, and other aircraft components.
Plastic working is possible with MA-X. In addition, due to its good weldability, general welding, such as metal arc, inert gas coating arc (TIG and MIG), etc. is possible. Resistance welding can be used as well.
Wrought forms of MA-X alloy are furnished in the solution heat-treated condition unless otherwise specified. MA-X alloy is solution heat-treated and rapid cooled.
Various shapes, such as flat-rolled plates, forgings, welding wire, wire, welded pipes and tubes, seamless pipes and tubes can be manufactured.
Information on specifications to which MA-X alloy can be ordered.
| Plates | Bars, Forgings | Pipes and Tubes | Joints |
|---|---|---|---|
| B435 | B572 | B619 | B366 |
| B622 | |||
| B626 |
| Plates | Bars, Forgings | Pipes and Tubes | Joints | SB-435 | SB-572 | SB-619 | SB-366 |
|---|---|---|---|
| SB-622 | - | ||
| SB-626 |
| Plates | Bars | Pipes and Tubes | Wires |
|---|---|---|---|
| H4551 | H4553 | H4552 | H4554 |
| Plates | Bars, Forgings | Pipes and Tubes |
|---|---|---|
| 5536 | 5754 | 5587 5588 |